THE ATMOSPHERE CONSTITUENTS FOR GAS CARBONITRIDING ANCHORAGE WEDGE
Le Thi Chieu1, Nguyen Duong Nam2*
1Hanoi University of Science and Technology
2Vietnam Maritime University, Haiphong city, Vietnam
*Corresponding Author Email: email@example.com
This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
Carbonitriding is a case-hardening process sin which carbon and nitrogen are increased in the surface layer of a lowcarbon parts at a temperature sufficient to render austenitenic steel. The followed by quenching and tempering to form martensite microstructure. In the comparison with carburizing, Carbonitriding is carried out at a lower temperature, for a shorter time and resultion finer microstructure. However, in our Industry, this method is not developed. The reason that the carbonitriding atmosphere is constituent unreasonably. On this paper, carbonitriding is prepared by mixture of Industrial gas, CO2; N2, NH3, with different ratio. The reasonable ratios is selected. Microstructure, microhardness are tested. This atmosphere is applied for carbonitriding for anchorage wedges, shows good result.